NATURAL RUBBER COATED ARAMID TIRE CORD

Tire cord fabric is a type of industrial fabric which is constructed using High Tenacity yarns in the warp direction and yarns of negligible resistance in weft direction which is used to hold warn yarns locked in their position. Tire cord coated fabrics provides fundamental properties such as controlled deformation, high strength, abrasion resistance, etc. Widely used by the tire industry, it is also employed for the rubber hose manufacture, air springs, expansion joints, among many other applications.

Fiber consisting of a long chain polymer containing amines and aromatic components. Infusible, does not melt, does not burn, does not soften. Besides it shows low emission of toxic gases while combustion. Certain aramid can decompose at 500 ° C, It is thermostable up to 250 ° C.
Natural rubber is to be considered as the sole non-synthetic rubber. This particular rubber can be recycled for the reutilization, mostly for the manufacturing of tires. New methods of recycling natural rubber are under development to diminish the ecological impact of used tires and other products.

Detaining excellent physical properties (elongation at break, tensile strength and abrasion) and presented in a widespread range of hardness, natural rubber has the best elasticity among all rubbers. Under ambient conditions (a mmix of the right temperature, sun exposition, rain and wind) natural rubbers shows almost perfect fatigue resistance, excellent compression and tear strength which makes it ideal for any dynamic applications.

General Properties min - max
Warp breaking strength 350 - 5000 daN/5cm
Weft breaking strength -
Warp elongation at break 2% - 5%
Weft elongation at break selon construction
Weight per sqm from 450 gr/m2
Thickness Upon request
Peeling strength Upon request
Continuous Temperature -50C° à 70C°
Point Temperature -50C° à 80C°

Properties

Fireproofed
Abrasion resistance
Non-skid
General Properties min - max
Warp breaking strenght 350 - 5000 daN/5cm
Weft breaking strenght 350 - 2000 daN/5cm
Warp elongation at break 2% - 5%
Weft elongation at break 2% - 5%
Weight per sqm 100 - 650
General Properties min - max
Hardness ShA 30 - 90 ShA
Hardness IRHD 30 - 90 IRHD
Tensile Strength 8 - 20
Elongation at break 100% - 900%
Operating temperature
Continuous Temperature -50 °C - 70 °C
Point Temperature -50 °C - 80 °C
Resistance
Solvent resistance
Acid resistance
oxygen ageing
Ozone ageing
light ageing
Cold ageing --
heat ageing --