NBR/PVC COATED POLYAMIDE TIRE CORD

Tire cord fabric is a type of industrial fabric which is constructed using High Tenacity yarns in the warp direction and yarns of negligible resistance in weft direction which is used to hold warn yarns locked in their position. Tire cord coated fabrics provides fundamental properties such as controlled deformation, high strength, abrasion resistance, etc. Widely used by the tire industry, it is also employed for the rubber hose manufacture, air springs, expansion joints, among many other applications.

Polyamide is a synthetic fiber formed of linear macromolecules having in the chain the recurring amide functional group. There are polyamides of low affinity and high affinity. They have low flammability, it starts to weaken at 180-200 ° C and melts at about 215-260 ° C. Good elasticity (greater than typical polyester). The polyamide yarn can have the strength of steel and fine wire of the spider. Depending on the weaving, the fabric may exhibit a very close silk appearance. Polyamide fabrics are often in the name of nylon which designated the base polyamide 6-6 whose current usage returns to generically polyamides.

As NBR is blended with PVC ageing resistance is improved. Likewise, flame, ozone and petrol resistance are largely improved.

Especially designed for particular applications, the formulation of this blend is destined to high-quality products that require an especial environmental resistance as much as the oil and fuel endurance.

General Properties min - max
Warp breaking strength 100 - 2000 daN/5cm
Weft breaking strength -
Warp elongation at break 10% - 30%
Weft elongation at break selon construction
Weight per sqm from 450 gr/m2
Thickness Upon request
Peeling strength Upon request
Continuous Temperature -20C° à 100C°
Point Temperature -20C° à 110C°

Properties

Fireproofed
Non-skid
Oil storage
Fuel storage
Ozone Resistance
Cold resistance
General Properties min - max
Warp breaking strenght 100 - 2000 daN/5cm
Weft breaking strenght 90 - 1400 daN/5cm
Warp elongation at break 10% - 30%
Weft elongation at break 10% - 30%
Weight per sqm 100 - 1100
General Properties min - max
Hardness ShA 30 - 90 ShA
Hardness IRHD 30 - 90 IRHD
Tensile Strength 8 - 20
Elongation at break 100% - 900%
Operating temperature
Continuous Temperature -20 C° - 100C°
Point Temperature -20 C° - 110C°
Resistance
Solvent resistance
Acid resistance
oxygen ageing
Ozone ageing
light ageing
Cold ageing --
heat ageing --
Available colors :
         
Fireproofing option.
  • Inflatable pipe plugs and shutters,
  • lifting bags.